1、第四章第四章 新拌砼的性质新拌砼的性质第四章 新拌砼的性质Fresh concrete is a mixture of water, cement, aggregate and admixture (if any). After mixing, operations such as transporting, placing, compacting and finishing of fresh concrete can all considerably affect the properties of hardened concrete. Fresh concrete is a mixture
2、 of第一节和易性一、砼的和易性定义二、和易性的测定三、影响和易性的因素四、调整和易性的措施第一节和易性一、砼的和易性定义The characteristics of fresh concrete(新拌混凝土) which affect full compaction are its consistency（稠度）, mobility（流动性） and compactability（易密性）. In concrete practice these are often collectively known as workability（工作性，和易性）. The ability of concr
3、ete to maintain its uniformity is governed by its stability（稳定性）, which depends on its consistency and its cohesiveness （粘聚性）. The characteristics of fresh c. For practical purposes workability generally implies the ease with which a concrete mix can be handled from the mixer to its finally compacte
4、d shape. The three main characteristics of the property are consistency, mobility and compactability. Consistency is a measure of wetness or fluidity. Mobility defines the ease with which a mix can flow into and completely fill the formwork or mould. Compactability is the ease with which a given mix
5、 can be fully compacted, all the trapped air being removed. . For practical purposes worka一 砼和易性的定义：指砼拌和物易于施工操作（拌和、运输、浇灌、捣实）并能保证质量均匀、成型密实的性能。它包括流动性(mobility )、粘聚性(cohesiveness)和保水性(water retentivity)三方面的含义。一 砼和易性的定义：指砼拌和物易于施工操作（拌和、运输、浇和易性包括三个方面： 1、流动性 指砼拌和物在自重或施工机械振捣的作用下，能够流动并均匀密实地填满模板的性能。 2、粘聚性 保持整
6、体均匀，不发生分层离析现象。 3、保水性 保持水分不使之泌出。和易性包括三个方面： 1、流动Three tests widely used for measuring workability are the slump, compacting factor and V-B consistometer tests.Slump test was developed by Chapman in the United States in 1913. A 300mm high concrete cone, prepared under standard conditions (BS 1881 : par
7、t 2) is allowed to subside and the slump of reduction in height of the cone is taken to be a measure of workability. Three tests widely used for me混凝土分层离析混凝土分层离析外分层外分层内分层内分层新拌混凝土泌水示意图新拌混凝土泌水示意图二、和易性的测定方法砼拌和物坍落度试验维勃稠度试验扩展度试验二、和易性的测定方法砼拌和物坍落度试验二、砼拌和物坍落度的测定二、砼拌和物坍落度的测定The three types of slump usually o
8、bserved are true slump, shear slump and collapse slump, as illustrated in figure 13.2. A true slump is observed with cohesive and rich mixes for which the slump is generally sensitive to variations in workability. A collapse slump is usually associated with very wet mixes and is generally indicative
9、 of poor quality concrete and most frequently results from segregation of its constituent materials. Shear slump occurs more often in leaner mixes than in rich ones and indicates a lack of cohesion which is generally associated with harsh mixes (low mortar content). The three types of slump usual第四章
10、新拌砼和易性课件第四章新拌砼和易性课件由坍落度的不同可将砼拌和物分为：大流动性砼 T 160 mm流 动 性 砼 100 150 mm塑 性 砼 50 90 mm低 塑 性 砼 10 40 mm由坍落度的不同可将砼拌和物分为：大流动性砼 拌合物的坍落度的选择：要根据结构构件截面尺寸大小、配筋疏密和施工捣实方法等来确定。拌合物的坍落度的选择：要根据结构构件截面尺寸大小、配筋疏密和三、影响和易性的因素Factors Affecting Workability ： 1、水泥浆的数量（水灰比不变）2、水泥浆的稠度（水泥量不变）3、砂率Sp（砂重占砂石总重百分率）4、水泥的品种和骨料的性质5、外加剂6、
11、时间和温度三、影响和易性的因素Factors Affecting Wo恒定用水量法则在配制混凝土时，当所用粗、细骨料的种类及比例一定时，为获得要求的流动性，所需拌合用水量基本是一定的，即使水泥用量有所变动(1m3混凝土水泥用量增减50100kg)时，也无甚影响。这一关系称为“恒定用水量法则”，恒定用水量法则在配制混凝土时，当所用粗、细骨料的种类及比例一第四章新拌砼和易性课件Sp图图水泥浆用量一定水泥浆用量一定SpC图T相同Sp图水泥浆用量一定SpC图合理砂率：是指在用水量及水泥用量一定的情况下，能使砼拌和物获得最大流动性，且能保持粘聚性、保水性良好时的砂率值。合理砂率：是指在用水量及水泥用量一
12、定的情况下，能使砼拌和物获第四章新拌砼和易性课件四、改善和易性的措施1、掺加外加剂2、改善骨料的级配3、在级配良好的情况下，尽可能采用较大粒径的骨料。4、选用合理砂率。5、在拌和砼时，当T过小，应保持W/C不变，增加水泥浆量。当T过大时，应保持Sp不变，增加砂石用量。四、改善和易性的措施1、掺加外加剂第四章新拌砼和易性课件第二节 含气量 拌合物中的气相分两类：拌合物中的气相分两类：1、浇筑振捣过程产生：粗大、连通。、浇筑振捣过程产生：粗大、连通。2、引气剂引入：均匀、稳定、封闭、独、引气剂引入：均匀、稳定、封闭、独立、细小（立、细小（200m）。）。 普通混凝土气相含量约为普通混凝土气相含量约
13、为1，加入引气，加入引气剂的混凝土气相含量约为剂的混凝土气相含量约为35。第二节 含气量 拌合物中的气相分两引起剂加入后含气量的作用1、和和易易性性：含含气气量量每每增增加加1时时，坍坍落落度度约约提提高高1cm，若若保保持持原原流流动动性性不不变变，则则可可减减水水约约610。同同时时由由于于微微小小气气泡泡的的存存在在，阻阻滞滞了了固固体体颗颗粒粒的的沉沉降降和和水水分分的的上上升升，加加之之气气泡泡薄薄膜膜形形成成时时消消耗耗了了部部分分水水分分，减减少少了了能能够够自自由由移移动动的的水水量量，从从而而使使混混凝凝土土拌拌合合物物的的保保水水性性得得到到改改善，泌水率显著降低，粘聚性也
14、良好。善，泌水率显著降低，粘聚性也良好。2、强强度度：含含气气量量每每增增加加1时时，抗抗压压强强度度将将降降低低46，抗抗折折强强度度降降低低23，而而且且随随龄龄期期的的延延长长，引引气气剂对强度的影响越显著。剂对强度的影响越显著。3、耐久性：耐久性： 抗渗性能比不掺引气剂的混凝土提高抗渗性能比不掺引气剂的混凝土提高50以上，以上， 抗冻性可提高抗冻性可提高3倍左右。倍左右。引起剂加入后含气量的作用1、和易性：含气量每增加1时，坍落第三节 湿表观密度 第四节 凝 结 时 间 将5mm及其以上的粗集料筛去 ，将剩余 砂浆置于规定容器内，振动密实，用规定的贯入阻力仪，测量贯入阻力和时间的变化关
15、系。贯入阻力为3.5MPa和28MPa时分别对应初凝时间和终凝时间。第三节 湿表观密度 第四节 凝假凝假凝 混凝土固相颗粒和水拌合后迅速产生硬化，但温度不上升。如再次搅拌拌合物又恢复流动性，并呈现正常凝结的现象，强度不明显降低。原因：1、石膏与水泥矿物粉磨时，由于磨机内温度升高，二水石膏脱水变成半水石膏。在混凝土各组成材料加水拌合时，半水石膏又迅速变成二水石膏。二水石膏凝结很快，但量较少。故重新搅拌时，结构很易被破坏。2、故相颗粒表面过量的电荷也会引起假凝。假凝 混凝土固相颗粒和水拌合后迅速1、水泥中铝酸三钙活性过高，石膏掺量不足而造成。2、铝酸三钙和石膏掺量均过高，形成大量钙矾石而导致速凝。3、外加剂会导致铝酸三钙水化过快而导致速凝。速凝速凝1、水泥中铝酸三钙活性过高，石膏掺量不足而造成。速凝