《Q345系列钢板合金减量化生产研究》由会员分享，可在线阅读，更多相关《Q345系列钢板合金减量化生产研究（4页珍藏版）》请在金锄头文库上搜索。
1、36 南钢科技与管理 2013年第4期 Q345系列钢板合金减量化生产研究 杨浩 陈晓泉 (技术质量部) 摘 要：介绍了中板厂轧后冷却设备的特点，利用轧后超快冷工艺的相变强化和细晶强化原理，结合现场实际 情况，对低合金铜板进行舍金减量化试验，成功开发出厚度小于50 nun的Q345系列降Mn合金铜板的生产工 艺。并根据生产初期实际问题进行工艺优化，最后生产出具有合金成本低、机械性能良好的低合金钢板。 关键词：快冷低合金铜板降Mn合金钢板工艺优化 Study 0U Reducing Alloy of Q345 Series Plate Yang Hao Chen Xiaoquan (Techno
2、logy&Quality Department) Abstract：The paper introduces the characteristics of fast cooling equipment at Medium Plate PlantWith the help of the themT of finegrain strengthening and transformation strengthening in fast cooling process after rolling，the experiment of reducing alloy for low alloy plate
3、has been done and the process of reducing the Mn alloy in Q345 series plate(50 mm)has been successfully developedBy optimizing the process in application at the initial stage，the low alloy steel plate with low cost and good mechanical properties can be produced Key words：fast cooling；low alloy plate
4、；reducing Mn alloy plate；process optimization Q345系列中碳低合金结构钢被广泛用于工程 结构、建筑领域，其成分设计简单，主要合金元素是 Mn。虽然Q345钢在国内各大钢厂都是较普通的产 品，但是其产量大，微小的降成本都能带来极大的利 润。中板厂以轧后快冷技术为核心，对Q345系列钢 板进行了降合金Mn工艺的开发，并固化合金减量化 后Q345钢板(后面简称降锰Q345钢)的生产工艺， 较大程度地节约了生产成本，为进一步挖掘快速冷 却工艺提供了重要依据。 1 超快速冷却设备的特点 中板厂轧后冷却设备具备高的冷却强度，可实 现轧后钢板大冷却速率范围，满足多品种系列规格 的中厚板产品冷却工艺；具备工艺拓宽、实现产品升 级、扩大品种范围的多种功能 。 2降锰Q345钢试生产工艺开发 21 成分设计 相对于原始Q345钢的化学成分，主要是降低了 0205的Mn合金，其化学成分见表1。 表1降锰Q345钢的化学成分 璺 ! 质量百分 018130035002O0150015 002005 22轧制工艺设计 为制定合理的控轧控冷工艺，对降锰Q345钢进 行CCT曲线基础数据实验，试验结果见图l。