1、.根据德国标准DIN50150, 以下是常用范围的钢材抗拉强度与维氏硬度、布氏硬度、洛氏硬度的对照表。抗拉强度维氏硬度布氏硬度洛氏硬度RmHVHBHRCN/mm 22508076.0-2708580.7-2859085.2-3059590.2-32010095.0-33510599.8-350110105-370115109-380120114-400125119-415130124-430135128-450140133-465145138-480150143-490155147-510160152-530165156-545170162-560175166-575180171-595185
2、176-610190181-625195185-640200190-660205195-675210199-690215204-705220209-720225214-740230219-755235223-77024022820.378524523321.3精选范本.80025023822.282025524223.183526024724.085026525224.886527025725.688027526126.490028026627.191528527127.893029027628.595029528029.296530028529.899531029531.0103032030
3、432.2106033031433.3109534032334.4112535033335.5111536034236.6119037035237.7122038036138.8125539037139.8129040038040.8132041039041.8135042039942.7138543040943.6142044041844.5145545042845.3148546043746.1152047044746.91555480(456)47.71595490(466)48.41630500(475)49.11665510(485)49.81700520(494)50.517405
4、30(504)51.11775540(513)51.71810550(523)52.31845560(532)53.01880570(542)53.61920580(551)54.11955590(561)54.7精选范本.1995600(570)55.22030610(580)55.72070620(589)56.32105630(599)56.82145640(608)57.32180650(618)57.866058.367058.868059.269059.770060.172061.074061.876062.578063.380064.082064.784065.386065.98
5、8066.490067.092067.594068.0HB 有两种一种是（钢球）另一种是（硬质合金球）用一定直径的钢球或硬质合金球，以规定的试验力（F）压入式样表面，经规定保持时间后卸除试验力，测量试样表面的压痕直径（L ）。布氏硬度值是以试验力除以压痕球形表面积所得的商。以HBS（钢球）表示，单位为N/mm2(MPa) 。其计算公式为：式中： F-压入金属试样表面的试验力，N；D-试验用钢球直径，mm ；d-压痕平均直径，mm。测定布氏硬度较准确可靠，但一般HBS 只适用于450N/mm2 （MPa）以下的金属材料，对于较硬的钢或较薄的板材不适用。在钢管标准中，布氏硬度用途最广，往往以压痕直径 d 来表示该材料的硬度，既直观，又方便。 布氏硬度试验还可用于有色金属和软钢，采用小直径球压头可以测量小尺寸和较薄材料。布氏硬度计多用于原材料和半成品的检测，由于压痕较大，一般不用于成品检测。举例： 120HBS10/1000/30 ：表示用直径10mm 钢球在 1000Kgf（ 9.807KN）试验力作用下， 保持 30s（秒）测得的布氏硬度值为120N/ mm2 （ MPa）。精选范本.HBS 是布氏硬度的一种,现在已经不在采用,测试标准已经更改,HBS 是钢球头 ,而现在均采用HBW 即HB,硬质合金钢球 ,橡胶邵氏硬度为HA 或 HD,HA 为软橡胶 ,HD 为硬橡胶精选范本