1、电解电容器纸浙江凯恩特种材料股份有限公司201003推荐精选1 电解电容器纸分类及基本特征型号紧度g/cm3厚度m抄造形式主要材料W10.6540,50,60圆网单层纸W 纤维0.8020,25,30,40长网单层纸0.8520,300.9020,25,30W20.7040长网W175-20+圆网双层复合纸高紧度层:W纤维低紧度层:W 纤维45,50,圆网W172-25+圆网双层复合纸60,70圆网W172-35+圆网双层复合纸0.8040,50长网W185-25+圆网双层复合纸60,70长网W185-35+圆网双层复合纸0.8540,50长网W190-25+圆网双层复合纸60,70长网W19
2、0-35+圆网双层复合纸WS20.8040,45,50,长网W185-25+圆网双层复合纸高紧度层:W纤维低紧度层: S+W 纤维60,70长网W185-35+圆网双层复合纸WD20.8040,45,50,长网W185-25+圆网双层复合纸高紧度层:W纤维低紧度层: D+W纤维60,70长网W185-35+圆网双层复合纸WM20.7035,40,45,50圆网W172-25+圆网双层复合纸高紧度层:W纤维低紧度层: M+W纤维60,70,90圆网W172-35+圆网双层复合纸WB20.6040,45,50圆网W165-20+圆网双层复合纸高紧度层:W纤维低紧度层: B+W纤维0.6560圆网W
3、170-20+圆网双层复合纸SM20.5050圆网+特种网双层复合纸S纤维+M纤维0.5540,50,600.6040,50,600.6540,50,60MJ20.2850特种网双层复合纸M+J纤维0.3040,500.3540,500.4040,500.4540,500.5040S20.5540,50圆网+特种网双层复合纸S纤维0.6040,500.6540,50推荐精选2 电解电容器纸的技术指标2.1 物理指标见下表 项指目 标型号紧度（绝干）g/cm3厚度m定量(绝干)g/m2纵向抗张强度不小于kN/m纵向吸液高度不小于 mm/10minESR参考值23 EG击穿电压参考值 VW10.6
4、50.03403.227.01.5051.29390504.032.51.6071.70420604.839.01.7081.984700.800.03221.617.61.20-1.10370252.020.01.40-1.51410302.424.01.50-1.92490403.232.01.80-2.596000.850.03221.618.71.30-420302.425.51.70-5500.900.03221.619.81.40-470252.022.51.50-520302.427.01.80-590W20.700.03403.228.01.6041.50400504.035.
5、01.8071.80460604.842.02.0092.38490705.649.02.20112.755400.800.03403.232.01.7032.18600504.040.02.0042.80655604.848.02.5053.35710705.656.02.7073.357700.850.03403.234.01.8022.45630504.042.52.0032.89690604.851.02.5043.45750WS20.800.03403.232.01.6031.85590504.040.02.0042.10620604.848.02.4052.65690705.656
6、.02.8073.35750WD20.800.03403.232.01.6031.82590453.636.01.8032.00610504.040.02.0042.12630604.848.02.4052.67690705.656.02.8073.29760推荐精选项 指 目标型号紧度（绝干）g/cm3 厚度m定量(绝干)g/m2纵向抗张强度不小于kN/m纵向吸液高度不小于mm/10minESR参考值23 EG 击穿电压参考值 VWM20.700.03403.228.01.6061.25400453.631.51.7071.31430504.035.01.8081.48450604.842.
7、02.00101.80490705.649.02.20122.10540806.456.02.60152.53600907.263.03.00183.02630WB20.600.03403.224.01.30120.93350453.627.01.40131.08380504.030.01.50141.204100.650.03604.839.01.60131.60450SM20.500.03504.025.01.20340.74-0.550.03403.222.01.30210.72-504.027.51.40300.88-604.833.01.50341.12-0.600.03403.22
8、4.01.30130.86-504.030.01.40211.15-604.836.01.50251.40-0.650.03403.226.01.4080.98-504.032.51.50131.20-604.839.01.60211.55-S20.550.03403.222.01.30220.69-504.027.51.40300.83-0.600.03403.224.01.40180.82-504.030.01.50221.14-0.650.03403.226.01.50150.98-504.032.51.60181.28-推荐精选项 指 目 标型号紧度（绝干）g/cm3 厚度m定量(绝干
9、)g/m2纵向抗张强度 不小于kN/m纵向吸液高度不小于mm/10minESR参考值23 EGGBL1KHZ100KHZMJ20.280.03504.0140.40500.291.080.190.300.03403.2120.40400.311.070.17504.0150.50500.381.100.200.350.03403.2140.40400.361.080.20504.017.50.50500.451.130.320.400.03403.2160.60350.431.160.28504.0200.80450.551.280.340.450.03403.2180.80300.481.2
10、40.32504.022.51.10400.621.300.360.500.03403.2201.30250.601.380.44备注：击穿电压因检测仪器变化，检测数值较以往有一定降低，但实际耐压值没有变化。 2.2 化学指标指 标单 位标准水溶性氯化物含量(mg/kg)2.0（按GB/T 2678.2进行）4.0（按3.7.2.2进行）8.0（按3.7.2.1进行）电导率(mS/m)1.4pH6.0-8.0铁微粒子 (0.080.1mm2) 大于0.1mm2个/1800cm25不许有水分%7.02.3 外观指标 2.3.1 纸张的纤维组织应均匀，不允许有硬质块、折子、孔洞、黄筋、皱纹和粗纤维
11、束；纸面应平整，不应有明显的匀度不良和透光现象。2.3.2 纸卷的端面应整齐，无波浪形以及其它机械损伤，两端面的松紧应一致，纸边无裂口，每卷纸接头不超过1个，接头处粘接牢固均匀并有明显标记。2.3.3 电解电容器纸为卷筒纸，卷筒直径为280mm300mm，纸的宽度为500mm和580mm，或符合合同规定。宽度尺寸偏差不应超过2mm。推荐精选3 试验方法3.1 测定条件以下项目测定，没有特别的要求，均按GB10739标准的测定条件即温度231相对湿度502%的条件下，将纸的材质平衡后再进行测定，客户对纸的测定时，也可将纸样放在温度100的条件下干燥10分钟，再在同上条件下进行测定。3.2 厚度测定取一定长度无皱纹的纸样，与纵向垂直将纸正面朝外叠成十层，从纸端的15mm内侧，圴摆5个测量点，用厚度仪测定各点厚度，取平均值即为试样的厚度，单位为um。3.3 紧度测定将上面测完厚度的纸样垂直切去两端约15mm宽的纸边，称其重量，并测出纸样的长和宽，按下式计