《材质成份表》由会员分享,可在线阅读,更多相关《材质成份表(1页珍藏版)》请在金锄头文库上搜索。
1、编制中五金有限公司编号SL-JS-74r r版次B/1审核常用铸钢材质成份表贝码1/1批准日期2009-12-3材质代号钢材标准化学成份(百分数)备注CSiSPMnNiCrMoCu其它CEA316ASTM A276-3160.081.000.0300.0452.0010.0-14.016.0-18.02.0-3.0奥氏体钢非铸材CF8MASTM A351 (2006)0.081.500.0400.0401.509.0-12.018.0-21.02.0-3.01.4408EN10213-4(2007)0.071.500.0300.0401.509.0-12.018.0-20.02.0-2.50.
2、501.4408DIN17445(1984)0.071.500.0300.0451.5010.0-12.018.0-20.02.0-3.0SCS14AJIS G5121(1991)0.081.500.0400.0401.509.0-12.018.0-21.02.0-3.0B304ASTM A276-3040.081.000.0300.0452.008.0-11.018.0-20.0奥氏体钢非铸材CF8ASTM A351 (2006)0.082.000.0400.0401.508.0-11.018.0-21.00.501.4308EN10213-4(2007)0.071.500.0300.040
3、1.508.0-11.018.0-20.00.501.4308DIN17445(1984)0.072.000.0300.0451.508.0-11.018.0-20.0SCS13AJIS G5121(1991)0.082.000.0400.0401.508.0-11.018.0-21.0MCN7MASTM A351 (2006)0.071.500.0400.0401.5027.5-30.519.0-22.02.0-3.03.0-4.0SCS23JIS G5121(1991)0.072.000.0400.0402.0027.5-30.019.0-22.02.0-3.03.0-4.0CWCBAST
4、M A216-WCB0.300.600.0450.0401.000.500.500.200.30V0.030.501.0619(GP240GH)EN10213-2(2007)0.18-0.230.30-0.600.0200.0300.50-1.200.400.300.120.30厚度V 28mm, S 0.030%1.0619(GS-C25)DIN17245(1987)0.18-0.230.30-0.600.0150.0200.50-0.800.30SCW410(SCW42)JIS G5102 (1991)0.220.800.0400.0401.50SCPH2JIS G5151 (1991)0
5、.300.600.0400.0401.000.500.250.250.501.00L316LASTM A276-316L0.031.000.0300.0452.0010.0-14.16.0-18.0|H0-3奥氏体钢非铸材,3MIASTM A351 CF3M0.031.500.0400.0401.509.0-13.017.0-21.012.0-3.01.4404EN10088-3(1995)0.031.000.0300.0452.0010.0-12.016.5-18.52.0-2.5N:0.11奥氏体钢非铸材1.4409EN10213-4(2007)0.031.500.0250.0352.00
6、9.0-12.018.0-20.02.0-2.50.50N:0.20SCS16AJIS G5121(1991)0.031.500.0400.0401.509.0-13.017.0-20.02.0-3.03304LASTM A276-304L0.031.000.0300.0452.008.0-12.018.0-20.0奥氏体钢非铸材CF3ASTM A351 (2006)0.032.000.0400.0401.508.0-12.017.0-21.00.501.4306EN10088-3(1995)0.031.000.0300.0452.0010.0-12.018.0-20.0N:0.11奥氏体钢非铸材1.4309EN10213-4(2007)0.031.500.0250.0352.009.0-12.018.0-20.00.50N:0.20SCS19AJIS G5121(1991)0.032.000.0400.0401.508.0-12.017.0-21.0