《台湾奇美ABS PA-747物性数据表》由会员分享，可在线阅读，更多相关《台湾奇美ABS PA-747物性数据表（2页珍藏版）》请在金锄头文库上搜索。
1、台湾奇美ABS PA-747物性数据表性能项目测试条件测试方法数值/描述单位机械性能拉伸强度(引张强度)ASTM D638/ISO 527385（5470）kg/cm(MPa)Lb/in2断裂伸长率ASTM D638/ISO 527-%拉伸模量ASTM D638/ISO 527-kg/cm(MPa)Lb/in2拉伸屈服伸长率(延伸率)ASTM D638/ISO 52730%拉伸断裂伸长率(延伸率)ASTM D638/ISO 527-%弯曲模量(弯曲弹性率)ASTM D790/ISO 1782200（310000）kg/cm(MPa)Lb/in2弯曲强度ASTM D790/ISO 178620（
2、8800）kg/cm(MPa)Lb/in2洛氏硬度ASTM D785R-108IZOD 缺口冲击强度1/4 23ASTM D256/ISO 17936（6.6）kgcm/cm(J/M)ftlb/in1/4 -30ASTM D256/ISO 17932（5.9）kgcm/cm(J/M)ftlb/in1/8 23ASTM D256/ISO 179-kgcm/cm(J/M)ftlb/in1/8 -30ASTM D256/ISO 17941（7.5）kgcm/cm(J/M)ftlb/inCharpy冲击强度23 （缺口）ASTM D256/ISO 179-kgcm/cm(J/M)ftlb/in-30（
3、缺口）ASTM D256/ISO 179-kgcm/cm(J/M)ftlb/in23（无缺口）ASTM D256/ISO 179-kgcm/cm(J/M)ftlb/in-30（无缺口）ASTM D256/ISO 179-kgcm/cm(J/M)ftlb/in物性性能比重（密度）ASTM D792/ISO 11831.03成型收缩率ASTM D955%熔融指数（流动系数）200/5kgASTM D1238/ISO 11331.2g/10min220/10kgASTM D1238/ISO 113313g/10min吸水率 23/24HASTM D570/ISO 62-%热性能热变形温度退火ASTM
4、 D648/ISO 7597（207）（）未退火ASTM D648/ISO 7586（187）（）维卡软化点ASTM D1525/ISO R306103（217）（）熔点-（）燃烧性（率）UL941、16“HB线性膨胀系数ASTM D696/ISO 11359-mm/mm.加工条件干燥条件于8590C下烘料约23小时加工温度射嘴180230C料筒前段190230料筒中段190230料筒后段180220熔体温度-模具温度30-70压力注塑压力-Mpa保压压力-Mpa背压-Mpa螺杆转速-rpm其他备注在射出周期中勿将热融胶长期停留在加热管中颜色-特性超高强度 射出成型用。用途安全帽头盔、摩托车档板、鞋后跟、雪地运动用品等。文档来源：ABS塑胶原料 http:/