1、 上 海 猛 特 金 属 制 品 有 限 公 司Shanghai Montan Metal Products Co., LtdWAVY WIRE 波纹钢纤维DESCRIPTION 描述Wavy wire is made from straight wire into wavy wire. And they has a high tensile strength, because they would be wiredrawn from wide into thin.波纹钢纤维是由直的钢丝加工成波纹状的纤维。由于是粗到细加工而成，因此具有高的抗拉强度。APPLICATIONS 应用They ca
2、n be used for construction industry, for example, concrete and mortar reinforcement etc.它们可用于建筑行业，如混凝土，灰浆增强等。CHARACTERISTICS 特征值Specification规格Tensile strength N/mm2Thickness 厚度mmWide 宽度MmLength 长度mmHeight波的高度mmStep of crimp 波距mmFW30 Min.800 0.40-0.80 2.10-2.75 30+-3 1.52.5 6.0-8.5FW40 Min.800 0.43-
3、0.90 2.25-2.85 40+-3 1.5-2.5 6.0-8.5FW50 Min.800 0.50-1.00 2.45-2.90 50+-3 1.5-2.5 6.0-8.5CR04W 550610 0.40-0.60 1.50-1.70 32+-3 0.4-0.6 3.8-4.6CR05 550610 0.40-0.60 1.50-1.70 32+-3 - -CR06H 11001300 Diameter:1 34+-1 - 4.0-6.0CR07H 9501150 Diameter:0.5 34+-1 - 4.0-6.0CR08H 550610 0.40-0.60 1.50-1.70
4、 32+-3 0.4-0.6 -CR09S 550-610 0.400.60 1.50-1.70 32+-3 0.4-0.6 -CHEMICAL COMPOSITION化学成份：0.07-0.10%C, 450弹性模量 Elastic Modulus (Mpa) 3500当量直径 Equivalent Dia (um) 100+-50断裂延伸性 Crack Elongation(%) 5-10吸水性 Water Absorbency 不吸水 NO熔点 Melting Point () 160-170应用领域 Applying Field混凝土路面，桥面，机场跑道，工厂地平等工程隧道，矿井的墙面
5、，顶板，等喷射混凝土工程河道，水坝等水利工程军事防护工程，码头护岸，桥墩等水泥混凝土预制件使用说明 Applying Instruction 长度选择： 一般工程混凝土中聚丙烯网状纤维的长度以 20mm 为宜。Length: Generally, the proper length of the fiber added into the concrete is 20mm.投料搅拌过程：先投入碎石，然后投入纤维，再投入砂子搅拌 2 分钟，使纤维充分打开，然后投入水泥和水按常规工艺搅拌均匀即可。也可按常规工艺投入顺序施工，但拌和搅拌时间应不少于 4 分钟，以使纤维充分混合。Mixing Proce
6、ss: Crushed stones, fibers and sands are out into the mixer in succession. After stirring for two minutes, fiber will fully spread and then add cement and water and stir normally. The addition of materials also can be put into as usual, but the stirring time should be properly prolonged to more 4 mi
7、nutes to make fiber completely mixed.成型养护过程：无特殊要求，可酌情延长震实时间 30 秒左右，抹面时应待混凝土表面稍微钝化后再进行，以免带出纤维，养护仍应按普通混凝土的要求进行。Shaping Maintenance: There is no special requirement. May along the vibrating time for 30s.The maintenance of the fiber concrete should be done same as the normal concrete.包装：常规包装每包 0。9KG，可根据
8、用户要求确定规格及包装型式。Package: 0.9kg per bag, may packed as customers requirement.聚丙烯单丝纤维POLYPROPYLENE MONOFILAMENT聚丙烯单丝纤维又称聚丙烯微纤维，及改性聚丙烯纤维，是我公司引进国外先进的喷丝生产技术，通过添加功能母料改性，并经特殊表面处理而成的，掺加到混凝土中后，具有分散性好，亲水性强，与水泥基体的裹握力强等优点。使用于各类水泥混凝土/砂浆工程的防裂增强，尤其适用于建筑物顶层，墙面，地面等水泥工程。The PP monofilament is also named as PP mini-fibe
9、r, is produced by refer-ring foreign advanced technology for fiber-spinning, modified by adding functional additive and special surface-treating. Mixing into cement concrete, it has many advantages such as good dispersing, better water affinity, strong linking force. It is suited to reinforce and cr
10、ack-resist to every kinds of cement concrete and mortar, specially used in engineering of building surface, floor, wall, etc.性能参数 Specification原料 Raw Material 聚丙烯 Polypropylene 断裂伸长率 Crack Elongation 20%+-5%纤维类型 Type 单丝 Monofilament 密度 Density 0.91+-0.10g/cm3纤维直径 Fiber Dia 0.02-0.05+-0.005mm 熔点 Melt
11、ing Point 160-170拉伸强度 Tensile Strength 450Mpa 抗酸碱性 Resistance to Acid, Alkali 强 Strong规格 Size 6,10,12,115,19,20,24,48mm 吸水性 Water Absorbency 不吸水 NO应用领域 Applying Field建筑防水层，地面处理，内外墙面处理；Be suitable for the water-proof layer, floor, innerouter wall of industrials and civil construction.工业厂房，仓库，停车场等表面防裂
12、增强处理；Increase cracking resistance on the surface of industrial workshop, warehouse and parking lot.游泳馆地面，游泳池，水池，水渠等防裂防渗增强处理；Increase cracking seepage resistance of the ground in natatorium, swimming pool, pond and ditch.公路，桥梁等混凝土路面工程；Highway, bridge and other roads.使用说明 Applying Instruction 长度选择：砂浆等
13、细骨料混凝土适用纤维长度 12mm 以下；粗骨料混凝土使用 12mm 以上纤维。Length: for mortar,12mm掺量：一般表面防裂，每立方米水泥混凝土/砂浆掺量不少于 0.9KG.Compounding Amount: for resisting the common cracks on surface, 0.9kg/m3 fibers to cement mortar are enough.配比及搅拌：不改变水泥，砂石骨料比例，可将水泥，骨料，添加剂及纤维一块加入，并加入水后搅拌，充分混合后即可使用，也可先与水泥及其它骨料干搅均匀后，在施工现场加水搅拌即可使用。Stirring
14、 Requirement: the proportion of cement, sand and aggregate is no need to be changed. Put cement, aggregate, additive and fiber together, then stir after adding enough water and time for stirring can be pro-longed for 2-3 minutes in order to make the compound mix completely. Also it can be mixed even
15、 with cement and other aggregates in advance, stirring by adding water at worksite before constructing.包装：每袋 0.9 或 1KG,可根据用户要求改变包装型式.Package: Common 0.9 or 1 kg per bag. May be modified with customers requirement.束状绞联聚丙烯纤维 TWISTED BUNDLE PP FIBER该产品是针对钢纤维而研制的替代品，与钢纤维相比具耐酸碱腐蚀，强度高，容易分散，易施工，对拌合设备无损伤等特点。聚合物粗纤维是以聚丙烯为原材料，通过特殊的并联拉丝和绞联成型工艺及表面处理后加工而成，具有断裂强度高，在混凝土中分散性好，握裹力强的优点，可替代钢纤维用于水泥混凝土的抗裂增强。性能参数 Specification密度 Density(g/cm3) 0.91+-0.01长度 Length (mm)